1008 Cold Rolled Steel Coil

1008 carbon steel coil is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms. 1008 in the cold rolled condition is used for exposed or unexposed parts where bending, moderate drawing, forming and welding may be involved.

WhatsApp：+86 15275315165

Email：Irene@shouyuansteel.com

Product Description

1008 Cold Rolled Steel Coil

1008 cold rolled steel coil contains about 1.2% manganese and 0.4% silicon. There are also nickel, aluminium, chromium, copper and molybdenum present in small quantities in the carbon steels. AISI 1008 carbon steel coil has excellent weldability, which includes projection, butt, spot and fusion, and brazeability. 1008 cold rolled steel coil is mainly used in automobile, printed metal pail, building, building materials, and bicycle, etc. Besides, it is the best material to manufacture organic coated strip.

Product Parameters

Product Name	1008 Cold Rolled Steel Coil
Production Process	Hot Rolling, Cold Rolling
Material Standards	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.
Width	100mm-3000mm
Length	1m-12m, or Customized Size
Thickness	0.1mm-400mm
Delivery Conditions	Rolling, Annealing, Quenching, Tempered or Standard
Surface Process	Ordinary, Wire Drawing, Laminated Film

Chemical Composition

Element	Content (%)
Iron, Fe	99.31-99.7 %
Manganese, Mn	0.30-0.50 %
Carbon, C	0.10 %
Sulfur, S	0.050 %
Phosphorous, P	0.040 %

Mechanical Properties

Properties	Metric	Imperial
Tensile strength	340 MPa	49300 psi
Yield strength (depending on temper)	285 MPa	41300 psi
Elastic modulus	190-210 Gpa	27557-30458 ksi
Bulk modulus (typical for steel)	200 GPa	29000 ksi
Shear modulus (typical for steel)	80.0 GPa	11600 ksi
Poisson’s ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	20 %	20 %
Reduction of area	45 %	45 %
Hardness, Brinell	95	95
Hardness, Knoop (converted from Brinell hardness)	113	113
Hardness, Rockwell B (converted from Brinell hardness)	55	55
Hardness, Vickers (converted from Brinell hardness)	98	98
Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)	55	55

Scope of Application

AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.

Product Application

Packaging and shipping

Factory Display

FAQ

1. What products do you supply?
We supply carbon steel, galvanized steel, pre-painted steel, stainless steel, copper, aluminum, and structural steel sections. Our product range includes sheets, coils, pipes, bars, strips, angles, channels, I-beams, and H-beams.

2. Can you provide customized specifications?
Yes. We can supply products in different materials, grades, thicknesses, widths, lengths, and surface finishes. Please send us your detailed specifications so we can confirm availability.

3. What processing services do you offer?
Depending on the product and project requirements, we can provide cutting, slitting, custom sizing, and other processing services. Please provide your drawings, dimensions, tolerances, and processing requirements with your inquiry.

4. How do you ensure product quality?
Products are supplied according to the material, dimensions, specifications, and quality requirements confirmed in the order. Please inform us before ordering if your project requires specific inspections, tests, or documents.

Product recommendation



WeChat

Tel

Irene@shouyuansteel.com



top